RTI uses cookies to offer you the best experience online. By clicking “accept” on this website, you opt in and you agree to the use of cookies. If you would like to know more about how RTI uses cookies and how to manage them please view our Privacy Policy here. You can “opt out” or change your mind by visiting: http://optout.aboutads.info/. Click “accept” to agree.
The impact of film thickness and substrate surface roughness on the thermal resistance of aluminum nitride nucleation layers
Su, Z., Freedman, J. P., Leach, J. H., Preble, E. A., Davis, R. F., & Malen, J. A. (2013). The impact of film thickness and substrate surface roughness on the thermal resistance of aluminum nitride nucleation layers. Journal of Applied Physics, 113(21), Article 213502. https://doi.org/10.1063/1.4808238
Thickness dependent thermal conductivity measurements were made on aluminum nitride (AlN) thin films grown by two methods on the (0001) surfaces of silicon carbide (SiC) and sapphire substrates with differing surface roughness. We find that the AlN itself makes a small contribution to the overall thermal resistance. Instead, the thermal boundary resistance (TBR) of 5.1 +/- 2.8 m(2)K/GW between the AlN and substrate is equivalent to 240 nm of highly dislocated AlN or 1450 nm of single crystal AlN. An order-of-magnitude larger TBR was measured between AlN films and SiC substrates with increased surface roughness (1.2 nm vs. 0.2 nm RMS). Atomic resolution TEM images reveal near-interface planar defects in the AlN films grown on the rough SiC that we hypothesize are the source of increased TBR. (C) 2013 AIP Publishing LLC.