Homoepitaxial N-polar GaN layers and HEMT structures grown by rf-plasma assisted molecular beam epitaxy

Abstract

The authors have investigated the growth and structural and electrical properties of homoepitaxial GaN layers and GaN/AlGaN heterostructures grown on free-standing, hydride vapor phase epitaxy grown, N-polar GaN: Fe substrates by rf-plasma molecular beam epitaxy. Secondary-ion mass spectroscopic analysis of unintentionally doped and Be-doped N-polar GaN layers indicate that oxygen is the dominant impurity in all layers and is largely insensitive to growth temperature in the range investigated (675 degrees C <T-S <760 degrees C). Transmission electron microscopy (TEM) indicates that threading dislocations are generated at the regrowth interface in these samples; in contrast to homoepitaxial growth on Ga-polar GaN, and that the density of threading dislocations diminishes as the growth temperature increases. However, examination by TEM indicates that threading dislocations are not generated at the regrowth interface of samples subjected to pregrowth substrate surface cleaning by gallium deposition and desorption and subsequent growth of ultrathin (15 degrees) initial AlN layers. N-polar GaN/AlGaN heterostructures grown on Be-doped homoepitaxial N-polar GaN buffers exhibit low buffer leakage and Hall mobilities up to 1680 cm(2)/Vs at sheet densities of 1.3 x 10(13) cm(-2). High electron mobility transistors have been fabricated on these structures; drain current densities over 700 mA/mm and breakdown voltages as high as 70V have been measured. (C) 2012 American Vacuum Society. [DOI:10.1116/1.3676175]